| Stainless Steel Plate304,304L,316L,317L,321,310S,409S,410,410S,420, 420J1, 430 |
|
|
| Model No.︰ | - |
| Brand Name︰ | - |
| Country of Origin︰ | - |
| Unit Price︰ | - |
| Minimum Order︰ | - |
|
|
|
|
|
| 304(L) |
| This is the widely used steel. It has the good corrosion resistance,thermal resistance and mechanical properties and is used for home appliances,construction materials and kitchenware,etc. |
| Chemical Composition (unite：wt%) |
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| 304 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
≤18.0-20.0 |
≤8.0-10.5 |
| 304L |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
≤18.0-20.0 |
≤8.0-10.5 |
| Mechanical Properties： |
| Grade |
YS（Mpa） |
TS（Mpa） |
EL（%） |
Hv |
|
|
|
| 304 |
≥205 |
≥520 |
≥40 |
≤200 |
|
|
|
| 304L |
≥175 |
≥480 |
≥40 |
≤200 |
|
|
|
| 316(L) |
| 316L stainless steel in a molybdenum bearing (2%~3%) austenitic. It is more resistant to general corrosion and pitting. It has higher creep resistance. |
| Chemical Composition (unite: wt%) |
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Others |
| SUS316 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
16.0～18.0 |
10.0～14.0 |
Mo：2～3 |
| SUS316L |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
16.0～18.0 |
12.0～15.0 |
Mo：2～3 |
| Mechanical Properties: |
| Grade |
YS（Mpa） |
TS（Mpa） |
（%） |
Hv |
|
|
|
|
| SUS316 |
≥205 |
≥520 |
≥40 |
≤200 |
|
|
|
|
| SUS316L |
≥175 |
≥480 |
≥40 |
≤200 |
|
|
|
|
| 316Ti |
| Similar to Grade 316L except that 316Ti has better high temperature strength, and mechanical strength. Used for equipment exposed to aggressive corrosive conditions and high temperature applications, including automotive flexible connectors, welded bellows, chimney liners, and flexible ducting. |
| Chemical Composition (unite: wt%) |
| Grade |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Others |
| 316Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
10.0～14.0 |
16.0～18.0 |
2.0～3.0 |
≥Ti5×C% |
| Mechanical Properties: |
|
|
|
|
|
| Grade |
YS（Mpa） |
TS（Mpa） |
EL（%） |
Hv |
|
|
|
|
|
| 316Ti |
≥205 |
≥520 |
≥40 |
≤200 |
|
|
|
|
|
| 317L |
| 317L is a low carbon version of 317 stainless. It possesses the same high strength and corrosion resistance and will produce stronger welds due to its low carbon content. Many users are shifting over to this alloy in lieu of 304 and 316 as availability and cost improves. |
| Features and Applications：Better seawater resistance and SCC resistance than that of 316L |
| Chemical Composition (unite: wt %) |
| Grade |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Others |
| 317L |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
11.0～15.0 |
18.0～20.0 |
3.0～4.0 |
- |
| Mechanical Properties: |
| Grade |
YS（Mpa） |
TS（Mpa） |
EL（%） |
Hv |
|
|
|
|
|
| 309S |
| 23Cr-13Ni known for good strength and corrosion resistance in continuous service temperatures up to 1000℃ |
| Chemical Composition (unite: wt%) |
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Others |
| 309S |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
22.0～24.0 |
12.0～15.0 |
- |
| Mechanical Properties: |
| Grade |
YS（Mpa） |
TS（Mpa） |
EL（%） |
Hv |
|
|
|
|
| 309S |
≥205 |
≥520 |
≥40 |
≤200 |
|
|
|
|
| 310S |
| 2310S : 22Cr - 20NiAs a kind of steel with superior high-temperature oxidation resistance and high-temperature strength by increasing the Cr and Ni contents, it is used for applications requiring heat-resistance, such as ships, machinery and heat exchangers, etc. |
| Chemical Composition (unite: wt%) |
| |
|
|
|
|
|
|
|
|
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Others |
| 310S |
≤0.08 |
≤1.50 |
≤2.00 |
≤0.045 |
≤0.030 |
24.0～26.0 |
19.0～22.0 |
- |
| Mechanical Features： |
| Grade |
YS（Mpa） |
TS（Mpa） |
EL（%） |
Hv |
|
|
|
|
| 310S |
≥205 |
≥520 |
≥40 |
≤200 |
|
|
|
|
|
|
|
|
| Specifications︰ | ASTM A240/A240M Specification for Heat-Resisting Chromium and Chromium-Nickel Stainless Steel Plate, Sheet and Strip for Pressure Vessels
ASTM A480/A480M Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip
ASTM A666-00 Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
JIS G4304 Hot Rolled Stainless Steel Plates, Sheets and Strip
JIS G4305 Cold Rolled Stainless Steel Plates, Sheets and Strip
JIS G4312 Heat-Resisting Steel Plates and Sheets
|
| Standard Met︰ |
Stainless Steel Sheet/Stainless Steel Plate
1 Thickness: 0.31-100 mm
2 Width: 1000/1219/1500/1800/2000mm (We can make special width according to customer's demand also)
3 Length: According to customers' reques
4 Material: 304, 304L, 316L, 321, 310S, 410, 410S, 420, 420J1, 430, 201, 202
5 Surface finish: NO. 1, 2B, BA, NO. 4, HL, 8k mirror
6 Application: Construction field, ships building industry, car making industry, petroleum&chemical industries, electricity industries, food processing and medical industry, boiler heat exchanger, machinery and hardware.
Stainless Steel Coil
Grade: 304,304L,321,321H,316,316L,317L,310S
or according to customer’s requirement.
Width 32mm-2200mm, or according to customer’s requirement.
Thickness 0.25-100mm, or according to customer’s requirement.
Standard: ASTM, GB, JIS, DIN, ASME, etc.
Surface finish: No. 2B, No. 3, No.4,BA
Application: construction field, building industry, petroleum & chemical industries, machinary, hardware fields, and so on.
Package detail: Wraps with kraft paper, steel strip bundled, wooden matting, or as per customers' requirements
|
|
|